Deutsch
Albanian
Arabic
Armenian
Azerbaijani
Belarusian
Bengali
Bosnian
Catalan
Czech
Danish
Deutsch
Dutch
English
Estonian
Finnish
Français
Greek
Haitian Creole
Hebrew
Hindi
Hungarian
Icelandic
Indonesian
Irish
Italian
Japanese
Korean
Latvian
Lithuanian
Macedonian
Mongolian
Norwegian
Persian
Polish
Portuguese
Romanian
Russian
Serbian
Slovak
Slovenian
Spanish
Swahili
Swedish
Turkish
Ukrainian
Vietnamese
Български
中文(简体)
中文(繁體)
ACS Applied Materials & Interfaces 2013-Apr

Surface wettability of macroporous anodized aluminum oxide.

Nur registrierte Benutzer können Artikel übersetzen
Einloggen Anmelden
Der Link wird in der Zwischenablage gespeichert
Josephus G Buijnsters
Rui Zhong
Natalia Tsyntsaru
Jean-Pierre Celis

Schlüsselwörter

Abstrakt

The correlation between the structural characteristics and the wetting of anodized aluminum oxide (AAO) surfaces with large pore sizes (>100 nm) is discussed. The roughness-induced wettability is systematically examined for oxide films grown by a two-step, high-field anodization in phosphoric acid of three different concentrations using a commercial aluminum alloy. This is done for the as-synthesized AAO layers, after various degrees of pore widening by a wet chemical etching in phosphoric acid solution, and upon surface modification by either Lauric acid or a silane. The as-grown AAO films feature structurally disordered pore architectures with average pore openings in the range 140-190 nm but with similar interpore distances of about 405 nm. The formation of such AAO structures induces a transition from slightly hydrophilic to moderately hydrophobic surfaces up to film thicknesses of about 6 μm. Increased hydrophobicity is obtained by pore opening and a maximum value of the water contact angle (WCA) of about 128° is measured for AAO arrays with a surface porosity close to 60%. Higher surface porosity by prolonged wet chemical etching leads to a rapid decrease in the WCA as a result of the limited pore wall thickness and partial collapse of the dead-end pore structures. Modification of the AAO surfaces by Lauric acid results in 5-30° higher WCA's, whereas near-superhydrophobicity (WCA ~146°) is realized through silane coating. The "rose petal effect" of strongly hydrophobic wetting with high adhesive force on the produced AAO surfaces is explained by a partial penetration of water through capillary action into the dead-end pore cavities which leads to a wetting state in-between the Wenzel and Cassie states. Moreover, practical guidelines for the synthesis of rough, highly porous AAO structures with controlled wettability are provided and the possibility of forming superhydrophobic surfaces is evaluated.

Treten Sie unserer
Facebook-Seite bei

Die vollständigste Datenbank für Heilkräuter, die von der Wissenschaft unterstützt wird

  • Arbeitet in 55 Sprachen
  • Von der Wissenschaft unterstützte Kräuterkuren
  • Kräutererkennung durch Bild
  • Interaktive GPS-Karte - Kräuter vor Ort markieren (in Kürze)
  • Lesen Sie wissenschaftliche Veröffentlichungen zu Ihrer Suche
  • Suchen Sie nach Heilkräutern nach ihrer Wirkung
  • Organisieren Sie Ihre Interessen und bleiben Sie über Neuigkeiten, klinische Studien und Patente auf dem Laufenden

Geben Sie ein Symptom oder eine Krankheit ein und lesen Sie über Kräuter, die helfen könnten, geben Sie ein Kraut ein und sehen Sie Krankheiten und Symptome, gegen die es angewendet wird.
* Alle Informationen basieren auf veröffentlichten wissenschaftlichen Forschungsergebnissen

Google Play badgeApp Store badge