Reliability and fatigue failure modes of implant-supported aluminum-oxide fixed dental prostheses.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

OBJECTIVE To investigate failure modes and reliability of implant-supported aluminum-oxide three-unit fixed dental prostheses (FDPs) using two different veneering porcelains. METHODS Thirty-six aluminum-oxide FDP frameworks were computer-aided designed and computer-aided manufactured and either

Dynamic fatigue and strength characterization of three ceramic materials.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

Fracture strength and fatigue parameters of three ceramic materials submitted to dynamic fatigue were evaluated. A machinable leucite-reinforced dental ceramic, aluminum oxide, and yttria-stabilized zirconia (YSZ) were tested. The inert strength of the materials was determined in air (25 degrees C)

Influence of zirconia surface treatments of a bilayer restorative assembly on the fatigue performance

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

Purpose: This study evaluated the influence of different surface treatments of zirconia used to enhance bonding with veneering porcelain, and thermocycling on the resistance to porcelain cracking and delamination during fatigue

The effect of film thickness and surface texture on the resistance of cemented extracoronal restorations to lateral fatigue loading.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

OBJECTIVE The aim of the present study was to assess the effect of cement-film thickness and surface texture (roughness) on the resistance of cemented crowns to dynamic lateral loading. METHODS Crown and abutment analogues were cemented using zinc-oxide-eugenol, zinc-phosphate, glass-ionomer, and

Corrosion-fatigue of laser-repaired commercially pure titanium and Ti-6Al-4V alloy under different test environments.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

This study evaluated the corrosion-fatigue life of laser-repaired specimens fabricated from commercially pure titanium (CP Ti) and Ti-6Al-4V alloy, tested under different storage conditions. For each metal, 30 dumbbell rods with a central 2.3 mm diameter were prepared by lost-wax casting with the

Effect of surface treatment on fatigue life of postceramic soldered joints.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

OBJECTIVE This research investigated the effect of surface treatment on the fatigue life of metal-ceramic postsoldering. METHODS Twenty cylindric specimens were cast in a metal-ceramic alloy. All specimens received appropriate heat treatment simulating ceramic application, although no porcelain was

Air-abrasion using new silica-alumina powders containing different silica concentrations: Effect on the microstructural characteristics and fatigue behavior of a Y-TZP ceramic.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

This study assessed the fatigue performance (biaxial flexure fatigue strength), surface characteristics (topography and roughness) and structural stability (t-m phase transformation) of a Y-TZP ceramic subjected to air-abrasion using new powders (7% and 20% silica-coated aluminum oxide particles) in

Fatigue performance of fully-stabilized zirconia polycrystals monolithic restorations: The effects of surface treatments at the bonding surface

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

This study evaluated the distinct conditioning effect of the intaglio surface of bonded fully-stabilized zirconia (FSZ) simplified restorations on the mechanical fatigue behavior of the set prior to and after aging. Ceramic disc shaped specimens (Ø= 10 mm and 1 mm thick) were randomly allocated into

Does Luting Strategy Affect the Fatigue Behavior of Bonded Y-TZP Ceramic?

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

To evaluate the effect of different luting strategies on the fatigue failure load (FFL) and stress distribution of Y-TZP disks luted to epoxy resin substrate. Y-TZP disks (diameter = 10 mm; thickness = 0.7 mm) were assigned to five groups according to the luting strategy (n = 15): CC: no zirconia

Grinding, polishing and glazing of the occlusal surface do not affect the load-bearing capacity under fatigue and survival rates of bonded monolithic fully-stabilized zirconia simplified restorations.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

This study aims to evaluate the effect of distinct surface treatments (grinding, polishing and glaze) of the occlusal surface of fully-stabilized zirconia (FSZ) simplified restorations bonded onto epoxy resin on the fatigue behavior of the restorations. Disc shaped specimens of FSZ (IPS e.max Zircad

Contact fatigue response of porcelain-veneered alumina model systems.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

Fatigue damage modes and reliability of hand-veneered (HV) and over-pressed (OP) aluminum-oxide layer structures were compared. Influence of luting cement thickness on mechanical performance was investigated. Sixty-four aluminum-oxide plates (10 × 10 × 0.5 mm) were veneered with hand built-up or

Reinforcement of Aluminum Oxide Filler on the Flexural Strength of Different Types of Denture Base Resins: An In vitro Study.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

BACKGROUND Acrylic resins have been used extensively for the fabrication of denture bases because of their aesthetic qualities, ease of manipulation and repairability. Flexural fatigue of the denture base has been shown to be a factor in the clinical failure of polymethyl methacrylate resin

Effect of water storage time and composite cement thickness on fatigue of a glass-ceramic trilayer system.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

OBJECTIVE Static Hertzian contact tests of monolayer glass-ceramics in trilayer configurations (glass-ceramic/cement/composite) have shown that thick cement layers lower strength. This study sought to test the hypothesis that thick resin cement layers lower mouth motion fatigue reliability for flat

Fatigue resistance of the bond of a glass-infiltrated alumina ceramic to human dentin.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

OBJECTIVE To evaluate the fatigue resistance of the bond between dentin and glass-infiltrated alumina ceramic, using different luting protocols. METHODS The null hypothesis is that the fatigue resistance varies with the luting strategy. Forty blocks of In-Ceram Alumina were prepared, and one surface

Fatigue Failure Load of Lithium Disilicate Restorations Cemented on a Chairside Titanium-Base.

Watumiaji waliosajiliwa tu ndio wanaweza kutafsiri nakala

Ingia / Ingia

OBJECTIVE To evaluate the fatigue failure load of distinct lithium disilicate restoration designs cemented on a chairside titanium base for maxillary anterior implant-supported restorations. METHODS A left-maxillary incisor restoration was virtually designed and sorted into 3 groups: (n = 10/group;

Iliyotangulia
1
2
Ifuatayo

Jiunge na ukurasa
wetu wa facebook

Herbal & Natural Medicine

Hifadhidata kamili ya mimea ya dawa inayoungwa mkono na sayansi

Inafanya kazi katika lugha 55
Uponyaji wa mitishamba unaungwa mkono na sayansi
Kutambua mimea kwa picha
Ramani ya GPS inayoshirikiana
Soma machapisho ya kisayansi yanayohusiana na utafutaji wako
Tafuta mimea ya dawa na athari zao
Panga maslahi yako na fanya tarehe ya utafiti wa habari, majaribio ya kliniki na ruhusu

Andika dalili au ugonjwa na usome juu ya mimea ambayo inaweza kusaidia, chapa mimea na uone magonjwa na dalili ambazo hutumiwa dhidi yake.
* Habari zote zinategemea utafiti wa kisayansi uliochapishwa