The insertion and removal of Li+ ions into Li-ion battery electrodes can lead to severe mechanical fatigue due to the repeated expansion and compression of the host lattice during electrochemical cycling. In particular, the lithium manganese oxide spinel (LiMn2O4, LMO) experiences a significant